Anode and Cathode Materials for Batteries

Bimetallic alloy nanomaterials are promising anode materials for potassium-ion batteries (KIBs) due to their high electrochemical performance. The most well-adopted fabrication method for bimetallic alloy nanomaterials is tube furnace annealing (TFA) synthesis, which can hardly satisfy the trade-off among granularity, dispersity and grain coarsening due to mutual constraints. Herein, we report a facile, scalable and ultrafast high-temperature radiation (HTR) method for the fabrication of a library of ultrafine bimetallic alloys with narrow size distribution (≈10–20 nm), uniform dispersion and high loading. The metal-anchor containing heteroatoms (i.e., O and N), ultrarapid heating/cooling rate (≈103 K s−1) and super-short heating duration (several seconds) synergistically contribute to the successful synthesis of small-sized alloy anodes. As a proof-of-concept demonstration, the as-prepared BiSb-HTR anode shows ultrahigh stability indicated by negligible degradation after 800 cycles. The in situ X-ray diffraction reveals the K+ storage mechanism of BiSb-HTR. This study can shed light on the new, rapid and scalable nanomanufacturing of high-quality bimetallic alloys toward extended applications of energy storage, energy conversion and electrocatalysis.

We report a flash Joule heating method for the rapid preparation of graphene-like materials. The L-GHS exhibited a uniform diameter of 200 nm and an ideal specific surface area of 670 m2 g−1. Meanwhile, the specific capacity of L-GHS remained at 942 mA h g−1 after 600 cycles (1 A g−1), which shows excellent electrochemical performance.

Graphite exhibits crystal anisotropy, which impedes the mass transfer of ion intercalation and extraction processes in Li-ion batteries. Herein, a dual-shock chemical strategy has been developed to synthesize the carbon anode. This approach comprised two key phases: (1) a thermal shock utilizing ultrahigh temperature (3228 K) can thermodynamically facilitate graphitization; (2) a mechanical shock (21.64 MPa) disrupting the π–π interactions in the aromatic chains of carbon can result in hybrid-structured carbon composed of crystalline and amorphous carbon. The optimized carbon (DSC-200–0.3) demonstrates a capacity of 208.61 mAh/g at a 10C rate, with a significant enhancement comparing with 15 mAh/g of the original graphite. Impressively, it maintains 81.06% capacity even after 3000 charge–discharge cycles. Dynamic process analysis reveals that this superior rate performance is attributed to a larger interlayer spacing facilitating ion transport comparing with the original graphite, disordered amorphous carbon for additional lithium storage sites, and crystallized carbon for enhanced charge transfer. The dual-shock chemical approach offers a cost-effective and efficient method to rapidly produce hybrid-structured carbon anodes, enabling 10C fast charging capabilities in lithium-ion batteries.